Préimh AISI 310S Cruach Dhosmálta Austenític sa tSín
Mar 18, 2026
Fág nóta
Comhdhéanamh Ceimiceach
| Eilimint | Comhdhéanamh (%) |
|---|---|
| Carbón (C) | ≤ 0.08 |
| Mangainéis (Mn) | ≤ 2.00 |
| sileacain (Si) | ≤ 1.50 |
| Fosfar (P) | ≤ 0.045 |
| Sulfar (S) | ≤ 0.030 |
| Cróimiam (Cr) | 24.0 - 26.0 |
| Nicil (Ni) | 19.0 - 22.0 |
| Nítrigin (N) | ≤ 0.10 |
| Iarann (Fe) | Iarmhéid |
⚙️ Airíonna Meicniúla
| Maoin | Luach |
|---|---|
| Neart Teanntachta (Teocht an tSeomra) | ≥ 515 MPa |
| Neart Toradh (Fritháireamh 0.2%) | ≥ 205 MPa |
| Fadú (tomhsaire 50mm) | ≥ 40% |
| Cruas (Brinell) | ≤ 217 HB |
| Cruas (Rockwell B) | ≤ 95 HRB |
| Fuinneamh Tionchair (Charpy V-notch) | ≥ 120 J |
| Modal Óg | 200 GPa |
| Teorainn Tuirse (107timthriallta) | 240 MPa |
🔬 Airíonna Fisiceacha
| Maoin | Luach |
|---|---|
| Dlús | 7.98 g / cm³ |
| Leáphointe | 1400-1450°C |
| Seoltacht Theirmeach (20°C) | 14.2 W/m·K |
| Comhéifeacht Leathnú Teirmeach (20-100°C) | 14.4×10-6/K |
| Comhéifeacht Leathnú Teirmeach (20-1000°C) | 18.0×10-6/K |
| Acmhainn Teasa Sonrach | 500 J/kg·K |
| Friotaíocht Leictreach (20°C) | 0.78 µΩ·m |
| Tréscaoilteacht Mhaighnéadach | 1.02 µH/m (Neamh-mhaighnéadach) |
| Cóimheas Poisson | 0.27-0.30 |