AISI 410 Cruach Dhosmálta sa tSín le haghaidh custome
Mar 23, 2026
Fág nóta
🧪 Comhdhéanamh Ceimiceach
| Eilimint | Comhdhéanamh (%) |
|---|---|
| Carbón (C) | ≤ 0.15 |
| Mangainéis (Mn) | ≤ 1.00 |
| sileacain (Si) | ≤ 1.00 |
| Fosfar (P) | ≤ 0.040 |
| Sulfar (S) | ≤ 0.030 |
| Cróimiam (Cr) | 11.5 - 13.5 |
| Nicil (Ni) | ≤ 0.75 |
| Iarann (Fe) | Iarmhéid |
⚙️ Airíonna Meicniúla
| Maoin | Coinníoll Annealed | Cruaite & Tempered |
|---|---|---|
| Neart Teanntachta | 485-620 MPa | 725-850 MPa |
| Neart Táirgeachta (0.2% fritháireamh) | 275-415 MPa | 550-690 MPa |
| Fadú (50mm) | ≥ 20% | ≥ 15% |
| Laghdú ar an Achar | ≥ 50% | ≥ 45% |
| Cruas (Brinell) | 155-217 HB | 235-285 HB |
| Cruas (Rockwell C) | - | 22-32 HRC |
| Fuinneamh Tionchair (Charpy V-notch) | 54-81 J | 27-54 J |
| Teorainn Tuirse (10&sup7; timthriall) | 240 MPa | 360 MPa |
🔬 Airíonna Fisiceacha
| Maoin | Luach |
|---|---|
| Dlús | 7.75 g / cm³ |
| Leáphointe | 1480-1530°C |
| Teas Sonrach (20°C) | 460 J/kg·K |
| Seoltacht Theirmeach (100°C) | 24.9 W/m·K |
| Leathnú Teirmeach (20-100°C) | 9.9×10-6/K |
| Leathnú Teirmeach (20-500°C) | 11.2×10-6/K |
| Friotaíocht Leictreach (20°C) | 0.57 µΩ·m |
| Tréscaoilteacht Mhaighnéadach | Feiromagnetic |
| Modal Leaisteachas | 200 GPa |
| Cóimheas Poisson | 0.27-0.30 |
📏 Sonraíochtaí Táirge
| Foirm Táirge | Raon Méid | Caighdeáin |
|---|---|---|
| Barraí Babhta | 6-300mm trastomhas | ASTM A276, A479 |
| Barraí Cearnóg | 10-150mm | ASTM A276 |
| Barraí Maol | 3-100mm tiubh, suas le 300mm ar leithead | ASTM A276 |
| Bileoga | 0.5-6mm tiubh, suas le 2000mm ar leithead | Tiománaí ASTM A240 |
| Plátaí | 6-100mm tiubh, suas le 3000mm ar leithead | Tiománaí ASTM A240 |
| feadáin | 6-219mm OD, balla 0.5-20mm | ASTM A268 |
| Críochnaigh Dromchla | Te rollta, fuar tharraingt, snasta | 2B, BA, Uimh.4, Uimh.8 |
| Caoinfhulaingt | ±0.1mm go ±1.0mm | EN 10029, ASTM A480 |
Glaoigh Linn